HT-202F Halogen-free Flame Retardants for Glass-fiber Reinforced PA66
Halogen-free Flame Retardants for Glass-fiber Reinforced PA66
 (HT-202F)
Product Description
1. Description
HT-202F is a kind of halogen-free flame retardant with the major flame retardant elements N and P, completely compliance with RoHs and REACH regulations. HT-202F has excellent compatibility in PA66 and can be well dispersed in PA66 resin, to make the glass-fiber reinforced PA66 reach UL 94V-0, high cost performance, excellent flame retardancy. The mechanical properties of PA66 with HT-202F have no significant difference compared to that of PA66 with Bromine-Antimony but a better electrical performance.
2. Physical and Chemical Properties
Item
Index
Item
Index
Appearance
White powder
Environmental requirements
Compliance with RoHS and REACH Regulations
Nitrogen content, %
35
Phosphorous content, %
11
Moisture, %
0.5
 
 
3. Recommendation
 
HT-202F
Loading
19%~21%
23%~25%
UL 94
  V-0 (3.2mm)
  V-0 (1.6mm)
4. Storage and Attention
Keep in dry, room temperature and moisture proof condition, preventing heat.
5. Packaging
Net weight 25kg/bag, Compound paper-plastic bag and inner aluminum foil.
Application Manual 
1. Typical formula
 
Formula adding HT-202F 
Formula adding BPS /ATO
PA66, %
46
44
Glass fiber, %
30
30
Flame retardant, %
24
26
2. Test Result
Item
Testing standards
Formula adding HT-202F  
Formula adding BPS/ATO
Flame retardancy (1.6mm)
UL94
V-0
V-0
GWFI (960℃)
GB/T 5619.10-2006
Pass
Pass
Tensile strength, MPa
GB/T 1040.5-2008
150         
144
Flexural strength, MPa
GB/T 9341-2008
190
172
Notched impact strength, kJ/m2
GB/T 1043.1-2008
8.9
10
Un-notched impact strength, kJ/m2
36.3
39.5
Electrical property (CTI), V
GB/T 4207-2003
325
<200
3. Conclusion
1) The flame retardancy of glass-fiber reinforced PA66 can reach UL 94(1.6mm)V-0 when adding 24% of HT-202F. 
2) The comprehensive properties of the glass-fiber reinforced PA66 with HT-202F are excellent, some properties are superior to that of PA66 with bromine-antimony.
3) HT-202F could completely substitute bromine-antimony flame retardants in glass-fiber reinforced PA66. 
4. Attention Concerned
(1) Control the temperature of extrusion and injection below 280℃; Using weaker shear screw combination, and the processing conditions should be in vacuum.
(2) Never contact with any strong oxidizing substances (such as antimony trioxide), otherwise causing the product discoloration.